Solvent-containing pastes containing in addition polyolefin wax

ABSTRACT

Solvent-containing pastes comprising a polyolefin wax component prepared from one or more olefins by catalysis using a single-site catalyst based on a complex of a transition metal from groups 5 to 8 of the Periodic System of the Elements, and use of these pastes.

[0001] The present invention relates to solvent-containing pastes comprising a polyolefin wax component prepared from one or more olefins by catalysis using a single-site catalyst based on a tri-pnicogen-cyclohexane complex of a transition metal from groups 5 to 8 of the Periodic System of the Elements. The present invention further relates to a process for preparing the solvent-containing pastes of the invention, to methods of caring for surfaces such as floors or wallcoverings comprising wood, ceramic, linoleum or modern plastics such as PVC, for coated metal surfaces such as exteriors of motor vehicles or boats, or of leather, e.g., shoes, boots, saddles or leather bags/suitcases, using the solvent-containing pastes of the invention.

[0002] Pastes containing solvent are used on a large scale to care for different kinds of surfaces, examples being floors, autos, or leather goods such as shoes. They comprise at least one wax, one or more solvents, and, optionally, additives. For care, the paste is applied to the surface to be treated, after which the solvent evaporates and leaves the wax as a fine film, which is occasionally referred to below as the protective coating. This film protects the surface thus treated both mechanically, for example, and against the action of the air.

[0003] Important properties for the user of the solvent-containing pastes are the paste hardness, a measure of the paste consistency, and also the surface quality, gloss, heat stability, and duration of drying. The duration of drying generally depends greatly on the nature and amount of the solvent. The desire is normally for a very low solvent content while retaining good processing properties, e.g., low paste viscosity.

[0004] Pastes containing solvent usually comprise two or more components. As the first component, use is made of the polyolefin waxes. However, further natural and synthetic waxes are usually added to the pastes. Examples of natural waxes are the carnauba waxes, imported from Brazil, and also montan wax raffinates, paraffin waxes or microwaxes. One known additive comprises metal stearates. An overview is given, for example, in Ullmann's Enyclopädie der technischen Chemie, 5th edition, Vol. A 28, p. 108 ff., Weinheim, 1996. was to provide a process for preparing such solvent-containing pastes, and finally to provide a method of caring for surfaces such as floors or wallcoverings comprising wood, ceramic, linoleum or modern plastics such as PVC, for coated metal surfaces such as exteriors of motor vehicles or boats, or for leather, e.g., shoes, boots, saddles or leather bags/suitcases, using such solvent-containing pastes.

[0005] We have found that this object is achieved by virtue of the fact that polyolefin waxes prepared from one or more olefins by catalysis using a single site catalyst based on a tri-pnicogen-cyclohexane complex of a transition metal from groups 5 to 8 of the Periodic System are especially suitable additives for the aforementioned area of application. The tri-pnicogen-cyclohexane complexes are preferably selected from 1,3,5-triazacyclohexane complexes, 1,3,5-triphosphacyclohexane complexes and 1,3-diaza-5-phosphacyclohexane complexes of a transition metal from groups 5 to 8 of the Periodic System of the Elements. Particularly preferred polyolefin waxes are those prepared with the aid of a complex of the formula I.

[0006] In formula I

[0007] the variables are defined as follows:

[0008] M is an element from the group consisting of V, Nb, Ta, Cr, Mo, W, Mn, Fe in oxidation state+3; preferably V, Cr or Mo, and with particular preference Cr;

[0009] Nu¹ to Nu³ are selected independently of one another from the pnicogens, preferably N or P; preferably, Nu¹ and Nu² are each N and with particular preference Nu¹ to Nu³ are each N.

[0010] X¹ to X³ are selected from

[0011] halogen such as fluorine, chlorine, bromine or iodine, chlorine and bromine being particularly preferred;

[0012] trifluoroacetate,

[0013] BF₄—, PF₆— or SbF₆—,

[0014] C₁-C₁₈ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, n-heptyl, iso-heptyl, n-octyl, n-nonyl, n-decyl, and n-dodecyl; preferably C₁-C₆ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, with particular preference C₁-C₄ alkyl such as methyl, ethyl, n-propyl and n-butyl;

[0015] C₃-C₁₂ cycloalkyl such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl and cyclododecyl; cyclopentyl, cyclohexyl and cycloheptyl are preferred,

[0016] C₇ to C₂₀ aralkyl, preferably C₇ to C₁₂ phenylalkyl such as benzyl, 1-phenethyl, 2-phenethyl, 1-phenylpropyl, 2-phenylpropyl, 3-phenylpropyl, 1-phenylbutyl, 2-phenylbutyl, 3-phenylbutyl and 4-phenylbutyl, with particular preference benzyl,

[0017] C₆-C₁₄ aryl such as phenyl, 1-naphthyl, 2-naphthyl, 1-anthryl, 2-anthryl, 9-anthryl, 1-phenanthryl, 2-phenanthryl, 3-phenanthryl, 4-phenanthryl and 9-phenanthryl, preferably phenyl, 1-naphthyl and 2-naphthyl, with particular preference phenyl;

[0018] C₁-C₁₂ alkoxy, preferably C₁-C₆ alkoxy such as methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, iso-butoxy, sec-butoxy, tert-butoxy, n-pentoxy, iso-pentoxy, n-hexoxy and iso-hexoxy, with particular preference methoxy, ethoxy, n-propoxy and n-butoxy, or

[0019] NR¹⁰R¹¹, where R¹⁰ and R¹¹ independently of one another are selected from hydrogen, C₁-C₁₂ alkyl, C₂-C₁₂ alkenyl and C₆-C₁₄ aryl, which are able to form a saturated or unsaturated 5- to 10-membered ring; preference is given to the dimethylamino, the diethylamino, the diisopropylamino, the methylphenylamino and the diphenylamino groups. Examples of amino groups containing saturated rings are the N-piperidyl group and the N-pyrrolidinyl group; examples of amino groups containing unsaturated rings are the N-pyrryl group, the N-indolyl group and the N-carbazolyl group.

[0020] Preferably, X¹ to X³ are identical; with very particular preference, X¹ to X³ are chlorine.

[0021] R¹ to R³ independently of one another are

[0022] C₁-C₁₈ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, n-heptyl, iso-heptyl, n-octyl, n-nonyl, n-Decyl, and n-dodecyl; preferably C₁-C₆ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, with particular preference C₁-C₄ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl and tert-butyl,

[0023] C₁-C₁₂ alkyl substituted one or more times by donor atoms, examples being noncyclic or cyclic ethers, alcohols, ketals, thioethers or amines; specific examples are methoxymethyl, ethoxymethyl, ethoxyethyl, β-hydroxyethyl, ω-ethoxypropyl, (2-ethylhexyloxy)propylidene, methoxyethoxypropylidene or ω-dimethylaminopropyl;

[0024] mono- or polyhalogenated C₁-C₁₂ alkyl groups such as fluoromethyl, difluoromethyl, trifluoromethyl, chloromethyl, dichloromethyl, trichloromethyl, bromomethyl, dibromomethyl, tribromomethyl, pentafluoroethyl, perfluoropropyl and perfluorobutyl, particular preference being given to fluoromethyl, difluoromethyl, trifluoromethyl and perfluorobutyl;

[0025] C₂-C₁₂ alkenyl, preferably C₂ to ω-C₈ alkenyl such as vinyl, allyl, but-3-en-1-yl, ω-pentenyl, ω-hexenyl, ω-heptenyl, and ω-octenyl;

[0026] C₃-C₁₂ cycloalkyl such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl and cyclododecyl; preference is given to cyclopentyl, cyclohexyl and cycloheptyl;

[0027] C₇ to C₂₀ aralkyl, preferably C₇ to C₁₂ phenylalkyl such as benzyl, 1-phenethyl, 2-phenethyl, 1-phenylpropyl, 2-phenylpropyl, 3-phenylpropyl, 1-phenylbutyl, 2-phenylbutyl, 3-phenylbutyl and 4-phenylbutyl, with particular preference benzyl,

[0028] C₆-C₁₄ aryl such as phenyl, 1-naphthyl, 2-naphthyl, 1-anthryl, 2-anthryl, 9-anthryl, 1-phenanthryl, 2-phenanthryl, 3-phenanthryl, 4-phenanthryl and 9-phenanthryl, preferably phenyl, 1-naphthyl and 2-naphthyl, with particular preference phenyl,

[0029] silyl SiR¹²R¹³R¹⁴, where R¹² to R¹⁴ independently of one another are selected from hydrogen, C₁-C₁₂ alkyl, C₇-C₁₅ aralkyl and C₆-C₁₄ aryl; preference is given to the trimethylsilyl, triethylsilyl, triisopropylsilyl, diethylisopropylsilyl, dimethylhexylsilyl, tert-butyldimethylsilyl, tert-butyldiphenylsilyl, tribenzylsilyl, triphenylsilyl and the tri-para-xylylsilyl groups; particular preference is given to the trimethylsilyl group and the tert-butyldimethylsilyl group;

[0030] siloxy OSiR¹²R¹³R¹⁴, where R¹² to R¹⁴ are selected independently of one another from hydrogen, C₁-C₁₂ alkyl, C₇-C₁₅ aralkyl and C₆-C₁₄ aryl; preference is given to the trimethylsilyloxy, triethylsilyloxy, triisopropylsilyloxy, diethylisopropylsilyloxy, dimethylthexylsilyloxy, tert-butyldimethylsilyloxy, tert-butyldiphenylsilyloxy, tribenzylsilyloxy, triphenylsilyloxy and the tri-para-xylylsilyloxy groups; particular preference is given to the trimethylsilyloxy group and the tert-butyldimethylsilyloxy group;

[0031] C₁-C₁₂ alkoxy, preferably C₁-C₆ alkoxy such as methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, iso-butoxy, sec-butoxy, tert-butoxy, n-pentoxy, iso-pentoxy, n-hexoxy and iso-hexoxy, with particular preference methoxy, ethoxy, n-propoxy and n-butoxy;

[0032] C₆-C₁₄ aryl substituted in turn by one or more C₁-C₁₂ alkyl, C₁-C₁₂ alkenyl, C₃-C₁₂ cycloalkyl, C₆-C₁₄ aryl, silyl SiR¹²R¹³R¹⁴, siloxy OSiR¹²R¹³R¹⁴ or C₁-C₁₂ alkoxy groups specified as above;

[0033] R⁴ to R⁹ independently of one another are

[0034] hydrogen,

[0035] halogen such as fluorine, chlorine, bromine or iodine, preference being given to chlorine and bromine;

[0036] C₁-C₁₈ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, n-heptyl, iso-heptyl, n-octyl, n-nonyl, n-decyl, and n-dodecyl; preferably C₁-C₆ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, with particular preference C₁-C₄ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl and tert-butyl,

[0037] C₁-C₁₂ alkyl substituted one or more times by donor atoms, examples being noncyclic or cyclic ethers, alcohols, ketals, thioethers or amines; specific examples are methoxymethyl, ethoxymethyl, ethoxyethyl, β-hydroxyethyl, ω-ethoxypropyl, (2-ethylhexyloxy)propylidene, methoxyethoxypropylidene or ω-dimethylaminopropyl;

[0038] mono- or polyhalogenated C₁-C₁₂ alkyl groups such as fluoromethyl, difluoromethyl, trifluoromethyl, chloromethyl, dichloromethyl, trichloromethyl, bromomethyl, dibromomethyl, tribromomethyl, pentafluoroethyl, perfluoropropyl and perfluorobutyl, particular preference being given to fluoromethyl, difluoromethyl, trifluoromethyl and perfluorobutyl;

[0039] C₂-C₁₂ alkenyl, preferably C₂ to ω-C₈ alkenyl such as vinyl, allyl, but-3-en-1-yl, ω-pentenyl, ω-hexenyl, ω-heptenyl, and ω-octenyl;

[0040] C₃-C₁₂ cycloalkyl such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl and cyclododecyl; preference is given to cyclopentyl, cyclohexyl and cycloheptyl;

[0041] C₇ to C₂₀ aralkyl, preferably C₇ to C₁₂ phenylalkyl such as benzyl, 1-phenethyl, 2-phenethyl, 1-phenylpropyl, 2-phenylpropyl, 3-phenylpropyl, 1-phenylbutyl, 2-phenylbutyl, 3-phenylbutyl and 4-phenylbutyl, with particular preference benzyl,

[0042] C₆-C₁₄ aryl such as phenyl, 1-naphthyl, 2-naphthyl, 1-anthryl, 2-anthryl, 9-anthryl, 1-phenanthryl, 2-phenanthryl, 3-phenanthryl, 4-phenanthryl and 9-phenanthryl, preferably phenyl, 1-naphthyl and 2-naphthyl, with particular preference phenyl,

[0043] silyloxy SiR¹²R¹³R¹⁴, where R¹² to R¹⁴ independently of one another are selected from hydrogen, C₁-C₁₂ alkyl, C₇-C₁₅ aralkyl and C₆-C₁₄ aryl; preference is given to the trimethylsilyl, triethylsilyl, triisopropylsilyl, diethylisopropylsilyl, dimethylhexylsilyl, tert-butyldimethylsilyl, tert-butyldiphenylsilyl, tribenzylsilyl, triphenylsilyl and the tri-para-xylylsilyl groups; particular preference is given to the trimethylsilyl group and the tert-butyldimethylsilyl group;

[0044] silyloxy OSiR¹²R¹³R¹⁴, where R¹² to R¹⁴ are selected independently of one another from hydrogen, C₁-C₁₂ alkyl, C₇-C₁₅ aralkyl and C₆-C₁₄ aryl; preference is given to the trimethylsilyloxy, triethylsilyloxy, triisopropylsilyloxy, diethylisopropylsilyloxy, dimethylthexylsilyloxy, tert-butyldimethylsilyloxy, tert-butyldiphenylsilyloxy, tribenzylsilyloxy, triphenylsilyloxy and the tri-para-xylylsilyloxy groups; particular preference is given to the trimethylsilyloxy group and the tert-butyldimethylsilyloxy group;

[0045] C₁-C₁₂ alkoxy, preferably C₁-C₆ alkoxy such as methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, iso-butoxy, sec-butoxy, tert-butoxy, n-pentoxy, iso-pentoxy, n-hexoxy and iso-hexoxy, with particular preference methoxy, ethoxy, n-propoxy and n-butoxy;

[0046] C₆-C₁₄ aryl substituted in turn by one or more C₁-C₁₂ alkyl, C₁-C₁₂ alkenyl, C₃-C₁₂ cycloalkyl, C₆-C₁₄ aryl, silyl SiR¹²R¹³R¹⁴, siloxy OSiR¹²OR¹¹R¹² or C₁-C₁₂ alkoxy groups specified as above.

[0047] Preferably, the radicals R¹ to R³ are each identical. Preferably R⁴, R⁶ and R⁸ are each identical, and preferably R⁴, R⁶ and R⁸ are each hydrogen. With very particular preference, R⁴ to R⁹ are hydrogen. The triazacyclohexane ligands necessary for synthesizing these very particularly preferred compounds may be synthesized with particular ease.

[0048] In one particular embodiment of the formula I, two adjacent radicals together form a saturated or unsaturated 4- to 9-membered ring; for example, two radicals may together be: C₃-C₉ alkylidene such as, for example, —(CH₂)₃— (trimethylene), —(CH₂)₄— (tetramethylene), —(CH₂)5— (pentamethylene), —(CH₂)₆— (hexamethylene), —CH₂—CH═CH—, —CH₂—CH═CH—CH₂—, —CH═CH—CH═CH—; and also cyclic aldols, ketals or amines such as, for example, —O—CH₂—O—, —O—CH(CH₃)—O—, —O—CH—(C₆H₅)—O—, —O—CH₂—CH₂—O—, —O—C(CH₃)₂—O—, —N(CH₃)—CH₂—CH₂—N(CH₃)—, —N(CH₃)—CH₂—N(CH₃)— or —O—Si(CH₃)₂—O—.

[0049] The preparation of the particularly preferred triazacycloalkane ligands for complexes of the formula I is known per se. Those for the synthesis of the very particularly preferred compounds of the formula I where R⁴ to R⁹ are each hydrogen and the radicals R¹ to R³ are each identical may be synthesized very effectively by mixing formaldehyde in the form, for example, of formalin solution with the associated amine R¹⁴—NH₂. Various synthesis pathways for these complex ligands are described, for example, in F. Weitl et al., J. Am. Chem. Soc. 1979, 101 2728; M. Takahashi, S. Takamoto, Bull. Chem. Soc. Japan 1977, 50, 3413; T. Arishima et al., Nippon Kagaku Kaishi 1973, 1119; L. Christiansen et al. Inorg. Chem. 1986, 25, 2813; L. R. Gahan et al., Aust. J. Chem. 1982, 35, 1119; B. A. Sayer et al., Inorg. Chim. Acta, 1983, 77, L63; K Wieghardt et al., Z. Naturforsch., 1983, 38b, 81 and I. A. Fallis et al., J. Chem. Soc., Chem. Commun. 1998, 665. Where one or two nitrogen atoms are to be replaced by P, the corresponding phosphines are reacted with formalin solution.

[0050] The metal complexes, especially the chromium complexes, may be obtained in a simple manner by reacting the corresponding metal salts such as metal chlorides or metal carbonyls, for example, with the ligand, as for example in P. Chaudhuri, K. Wieghardt, Prog. Inorg. Chem. 1987, 35, 329 or G. P. Stahley et al., Acta Crystall. 1995, C51, 18.

[0051] In order that above complexes of the formulae I are catalytically active, they are activated with a cation-forming compound. Suitable cation-forming compounds are selected aluminum or boron compounds having electron withdrawing radicals (e.g. trispentafluorophenylborane, trispentafluorophenylaluminum, N,N-dimethylanilinium tetrakispentafluorophenylborate, tri-n-butylammonium tetrakispentafluorophenylborate, N,N-dimethylanilinium tetrakis(3,5-bisperfluoromethyl)phenylborate, tri-n-butylammonium tetrakis(3,5-bisperfluoromethyl)phenylborate, and tritylium tetrakispentafluorophenylborate). These activators for complexes of the formulae I are described in DE-A 199 35 407, in PCT/EP 0002716, and in Angew. Chem. Int. Ed., 1994, Vol. 33, p. 1877. Preference is given to dimethylanilinium tetrakispentafluorophenylborate, tritylium tetrakispentafluorophenylborate, and trispentafluorophenylborane.

[0052] Where boron or aluminum compounds are used as activators for the complexes of formula I, they are generally employed in a molar ratio of from 1:10 to 10:1, based on M; preferably from 1:2 to 5:1, and with particular preference 1:1.5 to 1.5:1.

[0053] Another suitable class of cation-forming compounds comprises the aluminoxanes of the formulae II a and b.

[0054] The structure of the aluminoxanes is not precisely known. They are products obtained by careful partial hydrolysis of aluminum alkyls (see DE-A 30 07 725). These products do not exist in pure form but are instead mixtures of open-chain and cyclic structures of type II a and b. These mixtures are presumed to exist in a dynamic equilibrium with one another.

[0055] In formulae II a and b, the radicals R¹⁵ independently of one another are

[0056] C₁-C₁₂ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl, n-heptyl, iso-heptyl, n-octyl, n-nonyl, n-decyl, and n-dodecyl; preferably C₁-C₆ alkyl such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, n-pentyl, iso-pentyl, sec-pentyl, neo-pentyl, 1,2-dimethylpropyl, iso-amyl, n-hexyl, iso-hexyl, sec-hexyl; methyl is particularly preferred;

[0057] C₃-C₁₂ cycloalkyl such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl and cyclododecyl; preference is given to cyclopentyl, cyclohexyl and cycloheptyl;

[0058] C₇ to C₂₀ aralkyl, preferably C₇ to C₁₂ phenylalkyl such as benzyl, 1-phenethyl, 2-phenethyl, 1-phenylpropyl, 2-phenylpropyl, 3-phenylpropyl, 1-phenylbutyl, 2-phenylbutyl, 3-phenylbutyl and 4-phenylbutyl, with particular preference benzyl, or

[0059] C₆-C₁₄ aryl such as phenyl, 1-naphthyl, 2-naphthyl, 1-anthryl, 2-anthryl, 9-anthryl, 1-phenanthryl, 2-phenanthryl, 3-phenanthryl, 4-phenanthryl and 9-phenanthryl, preferably phenyl, 1-naphthyl and 2-naphthyl, with particular preference phenyl; and

[0060] n is an integer from 0 to 40, preferably from 1 to 25, and with particular preference from 2 to 22.

[0061] In the literature, cagelike structures are also discussed for aluminoxanes (Y. Koide, S. G. Bott, A. R. Barron Organometallics 1996, 15, 2213-26; A. R. Barron Macromol. Symp. 1995, 97, 15-25). Irrespective of the actual structure of the aluminoxanes, they are suitable activators for complexes of transition metals of the formulae I.

[0062] Mixtures of different aluminoxanes are particularly preferred activators in those cases where polymerization is conducted in a solution of a paraffin, n-heptane or isododecane, for example. One particularly preferred mixture is the COMAO available commercially from Witco GmbH, having a formula of [(CH₃)_(0.9)(iso-C₄H₉)_(0.1)AlO]_(n).

[0063] To activate the complexes of formula I with aluminoxanes generally requires an excess of aluminoxane, based on M. Rational M:AI molar ratios range from 1:10 to 1:10 000, preferably from 1:50 to 1:1000, and with particular preference from 1:100 to 1:500.

[0064] The chosen complex of the formulae I and the cation-forming compound together form a catalyst system. By adding one or more further aluminum alkyl compounds of the formula Al(R¹⁵)₃ it is 10 possible to increase further the activity of this catalyst system.

[0065] Aluminum alkyls of the formula Al(R¹⁵)₃ or aluminoxanes may also act as molecular mass regulators. Another effective molecular mass regulator is hydrogen. The molecular mass may be regulated with particular effect by the reaction temperature and the residence time.

[0066] Modern large-scale industrial preparation processes for polyolefin waxes are solution processes, suspension processes, bulk polymerization processes in liquid or supercritical monomer, and gas phase processes, the latter being either stirred gas phase or gas-phase fluidized bed processes.

[0067] In order that the complexes of the formulae I may be used in suspension processes, bulk polymerization processes or gas phase processes, it is advantageous to immobilize them on a solid support. Otherwise, morphological problems of the polymer (crumbs, wall deposits, blockages in pipes or heat exchangers) may occur, forcing shutdown of the plant.

[0068] Catalyst systems comprising complexes of the formulae I and activator may be effectively deposited on a solid support. Examples of suitable support materials are porous metal oxides, of metals from groups 2 to 14 or mixtures thereof, and also sheet silicates, and also solid halides of metals from groups 1, 2 and 13, and polymers such as, for example, polyethylene or polypropylene. Preferred examples of metal oxides from groups 2 to 14 are SiO₂, B₂O₃, Al₂O₃, MgO, CaO and ZnO. Preferred sheet silicates are montmorillonites or bentonites; preferred halides are MgCl₂ or amorphous AlF₃.

[0069] Particularly preferred support materials are spherical silica gels and alumosilicate gels of the formula SiO₂, Al₂O₃, where a is generally a number in the range from 0 to 2, preferably from 0 to 0.5. Silica gels of this kind are available commercially, e.g., Silica Gel 332, Sylopol® 948 or Sylopol 952 or S 2101 from W. R. Grace or ES 70X from Crosfield.

[0070] Proven particle sizes for the support material comprise average particle diameters of from 1 to 300 μm, preferably from 20 to 80 μm, the particle diameter being determined by means of known methods such as sieve methods. The pore volume of these supports is from 1.0 to 3.0 ml/g, preferably from 1.6 to 2.2 ml/g, and with particular preference from 1.7 to 1.9 ml/g. The BET surface area is from 200 to 750 m²/g, preferably from 250 to 400 m²/g.

[0071] In order to remove impurities, especially moisture, adhering to the support material, the support materials may be heated out prior to doping, suitable temperatures being from 45 to 1000° C. Temperatures of from 100 to 750° C. are particularly suitable for silica gels and other metal oxides; for MgCl₂ supports, temperature ranges from 50 to 100° C. are preferred. This heating out should take place over a period of from 0.5 to 24 hours, heatout times of from 1 to 12 hours being preferred. The pressure conditions are not critical per se; heating out may take place under atmospheric pressure. Advantageously, however, use is made of reduced pressures of from 0.1 to 500 mbar; a particularly advantageous range is from 1 to 100 mbar and a very particularly advantageous range from 2 to 20 mbar. Chemical pretreatment of the support material is another possibility.

[0072] The general procedure for doping the catalyst is to slurry the support material in a suspension medium and to combine this suspension with the solution of a complex of the formula I and of the activator. The volume of the suspension medium is from 1 to 20 times the pore volume of the catalyst support. Subsequently, the catalyst may be separated from the suspension medium by means of an appropriate method, such as filtration, centrifugation or evaporation.

[0073] For better control of the morphology, the catalyst may be prepolymerized with small amounts of monomer prior to the polymerization proper. The prepolymerization can be terminated by adding a reversible catalyst poison or by ending the feed of monomer, and the prepolymerized catalyst may subsequently be added to the polymerization unit.

[0074] Suitable monomers include the following olefins: ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 1-decene or 1-undecene, ethylene being particularly preferred.

[0075] Suitable comonomers include a-olefins, such as from 0.1 to 20 mol% of 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-octene, 1-decene or 1-undecene. Isobutene, however, is also a suitable comonomer.

[0076] In order to prevent the electrostatic charging of the olymerization unit or of the product that is occasionally observed with polymerizations, an antistat may be added to the reaction mixture. Suitable antistats are dilute solutions of aliphatic alcohols, such as isopropanol, in paraffins such as n-heptane, for example. Further suitable antistats are available commercially as Stadis® products from DuPont.

[0077] To prepare the solvent-containing pastes of the invention, an advantageous procedure is to melt the polyolefin wax and then to add preheated solvent. In this operation it is advantageous to effect thorough mixing of the hot paste, which can be achieved by stirring, shaking or similar operations known to the skilled orker. Solvents used are advantageously petroleum spiritis or turpentine oil.

[0078] As a quantitative proportion, more than 20 percent by weight, preferably more than 25% by weight and, with particular preference >30% of polyolefin wax is chosen. It is also possible to use less wax, although in that case the solvent-containing pastes have high solvent contents, which is undesirable.

[0079] Thereafter, further constituents are optionally added; examples are montan waxes, carnauba waxes, metal stearates, antioxidants such as the Irganox® products from Ciba for example, or paraffin waxes.

[0080] Subsequently, the mixture is left for a period of at least 1 minute and not more than one hour with stirring at a temperature just above the solidification point, and in the latter operation the mixture is cooled. The target temperature used is room temperature or colder, but not below −78° C. After 24 hours, the paste hardness is measured.

WORKING EXAMPLE

[0081] Preparation of the complex (n-C₁₂H₂₅NCH₂)₃CrCl₃ and polymerization of ethylene are described fundamentally in DE-A 199 35 407, in PCT/EP 0002716, and in Angew. Chem. Int. Ed., Vol. 33, 1994, p. 1877.

[0082] In a 10 liter steel autoclave (from Büchi), 50 mg (67 μmol) of (n-C₁₂H₂₅NCH₂)₃CrCl₃, dissolved in toluene, were activated with 14 ml of 30% MAO from Witco, the Al:Cr ratio set being 1000:1. 4 l of isobutane and 80 l (3.8 mol) of hydrogen were injected, and the autoclave was then heated to 90° C. Subsequently, 40 bar of ethylene were injected and polymerization was conducted for 30 minutes, the pressure being maintained at 40 bar by adding further ethylene.

[0083] The polymerization was terminated by letting down the autoclave.

[0084] Yield: 460 g, corresponding to an activity of 14,000 kg of PE(mol Cr·h).

[0085] The wax thus obtained had the following properties: melting point 128.5° C.; M_(w): 5200 g, M_(n): 2100 g. M_(w)/M_(n)=2.5.

[0086] The application example was conducted in analogy to Examples 1 and 2 of EP 0 916 700, in order to ensure good comparability of the results:

[0087] 20 parts by weight of wax were melted and brought to a temperature of 140° C. 100 parts by weight of petroleum spirit (boiling range 140-180° C.) were added with stirring. The wax solution was first brought to a temperature of 2° C. above the melting point of the wax and then poured into a can which had been cooled to 16° C. (bottom cooling). The solvent-containing paste thus obtained was stored at room temperature for 24 hours, after which the paste hardness was measured. Melt viscosity Paste Paste Melting at 140° C. viscosity hardness Test Wax point [cst] [mPa · s] [mbar]  1 DE 199 35 407 125.3 670 370 450 C1 Ziegler-Natta¹ 124.2 590 450 390 C2 EP 0 916 700 126.4 710 1310 210 C3 High pressure² 111.3 690 1109 90 

We claim:
 1. A solvent-containing paste comprising a polyolefin wax component prepared from one or more olefins by catalysis using a single-site catalyst based on a tri-pnicogen-cyclohexane complex of a transition metal from groups 5 to 8 of the Periodic System of the Elements.
 2. A solvent-containing paste as claimed in claim 1, wherein the tri-pnicogen-cyclohexane complex is selected from 1,3,5-triazacyclohexane complexes, 1,3,5-triphosphacyclohexane complexes and 1,3-diaza-5-phosphacyclohexane complexes of a transition metal from groups 5 to 8 of the Periodic System of the Elements.
 3. A solvent-containing paste as claimed in either of claims 1 and 2, wherein the single-site catalyst comprises as catalytically active component a Cr complex.
 4. A process for preparing a solvent-containing paste, which comprises dissolving in a hydrocarbon a polyolefin wax prepared from one or more olefins by catalysis using a single site catalyst based on a tri-pnicogen-cyclohexane complex of a transition metal from groups 5 to 8 of the Periodic System and then cooling the solution.
 5. A method of caring for floors and wallcoverings comprising wood, ceramic, linoleum or plastics, which comprises treating said floors or wallcoverings with one or more solvent-containing pastes as claimed in any of claims 1 to
 3. 6. A method of caring for metal surfaces of motor vehicles and boats, which comprises treating said metal surfaces with one or more solvent-containing pastes as claimed in any of claims 1 to
 3. 7. A method of caring for leather, which comprises treating the leather goods with one or more solvent-containing pastes as claimed in any of claims 1 to
 3. 